Enhanced mechanical properties of ZrO 2-Al 2O 3 dental ceramic composites by altering Al 2O 3 form
Highlights • Addition of Al 2 O 3 result in decrease in sintering shrinkage and relative density. • Different forms of Al 2 O 3 in Al 2 O 3…
Effect of finishing/polishing techniques and low temperature degradation on the surface topography, phase transformation and flexural strength of ultra-translucent ZrO 2 ceramic
Highlights • The LTD also significantly increased the fracture resistance of zirconia. • The fracture resistance was significantly lower in all groups that were glazed. • The groups were treated…
Adhesion to high-performance polymers applied in dentistry: A systematic review
Abstract Objective The aim of this systemic review, conducted in accordance with the PRISMA statement, was to investigate the impact of surface pretreatments on the bonding strength of high performance…
Outcomes of ultra-fast (3 s) photo-cure in a RAFT-modified resin-composite
Highlights • Effective photo-curing for 3 s at high radiant emittance is connected to a modification of the polymerization mechanism in a dimethacrylate resin-based composite (RBC) by incorporation of a…
Load-bearing capacity of CAD/CAM 3D-printed zirconia, CAD/CAM milled zirconia, and heat-pressed lithium disilicate ultra-thin occlusal veneers on molars
Highlights • Occlusal veneers can be reliably produced by 3D-printing with the Lithography-based Ceramic Manufacturing process. • 3D-printed zirconia, milled zirconia and heat-pressed lithium disilicate can be recommended as material…
The adverse effects of tungsten carbide grinding on the strength of dental zirconia
Highlights • Grinding dental zirconia with tungsten carbide burs causes a significant reduction of the biaxial flexural strength. • This reduction was attributed to ultra-structural subsurface micro-cracks observed to have…
Development of novel dental restorative composites with dibasic calcium phosphate loaded chitosan fillers
Highlights • Electrospraying was successful to obtain chitosan particles encapsulated with and without DCPA. • Antimicrobial effect was by due attributed to direct contact of the bacteria with exposed with…
Cyclic contact fatigue resistance of ceramics for monolithic and multilayer dental restorations
Abstract Objective To evaluate the cyclic contact fatigue resistance and failure mode of ceramics for monolithic and multilayer restorations. Methods Ceramic structures (10 mm × 1.8 mm) were fabricated as…