22: Direct Gold Restorations

Direct Gold Restorations

Gregory E. Smith

Direct Golds and Principles of Manipulation

Several types of dental restorative materials are currently available. Generally, they are grouped into categories such as amalgam, cast gold, tooth-colored material, dental porcelain, porcelain-fused-to-metal (PFM), and direct gold. Direct gold is a gold restorative material that is manufactured for compaction directly into prepared cavities. Two types of direct gold are manufactured for dental use: gold foil and powdered gold. These gold materials differ in their metallurgic structure.

Pure gold has been in use in dentistry in the United States for more than 100 years.16 Various techniques have been advanced for its use in the restoration of teeth. It is generally agreed that this noble metal is a superior restorative material for treatment of many small lesions and defects in teeth, given sound pulpal and periodontal health. Success is achieved with direct gold restorations if meticulous care is given to an exacting technique in tooth preparation design and material manipulation. Direct gold restorations can last for a lifetime if attention is paid to details of restorative technique and to proper home care. The longevity of direct gold restorations is a result of the superb biocompatibility of gold with the oral environment and its excellent marginal integrity.

This chapter discusses the various forms of direct gold presently available and explains the principles required for their manipulation. The principles of tooth preparation are reviewed as they are applied to direct gold restorations. Class I, V, and III preparations and their restoration are considered in detail.

Materials and Manufacture

Several physical types of direct-filling gold have been produced.7 All are “compactable” in that they are inserted into tooth preparations under force and compacted or condensed into preparation line and point angles and against preparation walls.

Gold foil is manufactured by beating pure gold into thin sheets. The gold foil is cut into 4 × 4 inch (10 × 10 cm) sheets and sold in books of sheets, separated by pages of thin paper. The books contain image oz or image oz of gold. The sheet of foil that weighs 4 g is termed No. 4 foil; the sheet weighing 3 g is termed No. 3 foil; and the sheet weighing 2 g is termed No. 2 foil. Because the 4 × 4 inch sheets are too large to be used in restorative procedures, they are rolled into cylinders or pellets before insertion into tooth preparations. (The gold foil referred to in the restorative sections of this chapter is in pellet form.)

Pellets of gold foil are generally rolled from image-inch, image-inch, image-inch, or image-inch sections cut from a No. 4 sheet of foil. The book of foil is marked and cut into squares or rectangles (Online Fig. 22-1, A). Each piece is placed on clean fingertips, and the corners are tucked into the center (see Online Fig. 22-1, B and C), and then the foil is lightly rolled into pellet form (see Online Fig. 22-1, D). In addition, cylinders of gold foil may be rolled from the segments of a sheet (see Online Fig. 22-1, A). After pellets of gold are rolled, they may be conveniently stored in a gold foil box (Online Fig. 22-2), which is divided into labeled sections for various sizes of pellets. Cylinders of foil and selected sizes of other types of gold also may be stored in the box. Preferential contamination is suggested by placing a damp cotton pellet dipped into 18% ammonia into each section of the box. This serves to prevent deleterious oxides from forming on the gold until it is used.

Powdered gold is made by a combination of chemical precipitation and atomization, with an average particle size of 15 mm (Online Fig. 22-3, A).8 The atomized particles are mixed together in wax, cut into pieces, and wrapped in No. 4 or No. 3 foil (see Online Fig. 22-3, B). Several sizes of these pellets are available. This product is marketed as Williams E-Z Gold (Ivoclar-Williams, Amherst, NY).

Cohesion and Degassing

Direct gold is inserted into tooth preparations under force. The purpose of the force is to weld the gold into restorations containing minimal porosity or internal void spaces.911 Welding occurs because pure gold with an absolutely clean surface coheres as a result of metallic bonding. As the gold is forced and compressed into a tooth preparation, succeeding increments cohere to those previously placed. For successful welding to occur during restoration, the gold must be in a cohesive state before compaction, and a suitable, biologically compatible compacting force must be delivered.

Direct gold may be either cohesive or noncohesive. It is noncohesive in the presence of surface impurities or wax, which prevents one increment of gold from cohering to another. The manufacturer supplies books of gold foil or pre-rolled cylinders in a cohesive or noncohesive state. E-Z Gold pellets are supplied with a wax coating that must be burned off before compaction.

Because gold attracts gases that render it noncohesive, such gases must be removed from the surface of the gold before dental compaction. This process usually is referred to as degassing or annealing and is accomplished by application of heat. The term degassing is preferable because the desired result is to remove residual surface contamination (although further annealing, resulting in additional internal stress relief or recrystallization, also may occur in this process). All direct-filling gold products are degassed immediately before use except when noncohesive foil is specifically desired. Under-heating during degassing should be avoided because it fails to render the gold surface pure. Over-heating also should be avoided because it may cause the gold to become brittle or melt and render it unusable. Degassing is accomplished by heating the gold foil on a mica tray over a flame or on an electric annealer or by heating each piece of gold over a pure ethanol flame (Online Fig. 22-4).

The advantage of the technique involving use of the pure ethanol flame is that each piece of gold is selected and heated just before insertion, and waste of gold is avoided. A careful technique is needed to degas an increment of gold in the flame correctly. The gold is passed into the blue inner core of the flame on the tip of a foil-passing instrument and held just until the gold becomes dull red, and then the instrument is withdrawn from the flame. After a few seconds are allowed for cooling, the gold is placed in the preparation. Although any of the three degassing procedures is satisfactory for gold foil, this is not the case for E-Z Gold. The E-Z Gold pellet must be heated image to 1 inch above the ethanol flame until a bright flame occurs (caused by ignition of the wax) and the pellet becomes dull red for 2 to 3 seconds, then it is withdrawn from above the flame.

Principles of Compaction

Direct-filling gold must be compacted during insertion into tooth preparations.12 With the exception of E-Z Gold, the compaction takes the form of malleting forces that are delivered either by a hand mallet used by the assistant or by an Electro-Mallet (McShirley Products, Glendale, CA) or a pneumatic mallet used by the dentist. E-Z Gold, because of its powdered form, may be compacted by heavy hand pressure delivered in a rocking motion with specially designed hand condensers.13,14 Successful malleting of the gold foil may be achieved with any of the currently available equipment. Some operators prefer the Electro-Mallet or the pneumatic mallet because a dental assistant is not required for the procedure.

A technique preferred by many clinicians uses a hand mallet to deliver light blows to a condenser held by the dentist (Online Fig. 22-5, A). This technique allows great control of malleting forces when variations are called for, and it allows for rapid change in condenser nibs, or tips, when a multitude of condensers is required. In any case, a suitable condenser must be stepped over the gold systematically to achieve a dense, well-compacted restoration (see Online Fig. 22-8).

Condensers are designed to deliver forces of compaction to direct gold. Condensers used in the handpieces of the Electro-Mallet or pneumatic mallet consist of a nib, or working tip, and a short shank (approximately 1 inch [2.5 cm] in length) that fits into the malleting handpiece. Condensers used with the hand mallet are longer (approximately 6 inches [15 cm]) and have a blunt-ended handle that receives light blows from the hand mallet.

Condenser nibs are available in several shapes and sizes (see Online Fig. 22-5, B). All have pyramidal serrations on the nib faces to prevent slipping on the gold. Condensers described in this chapter are (1) the round condensers, 0.4 to 0.55 mm in diameter; (2) the Varney foot condenser, which has a rectangular face that is approximately 1 to 1.3 mm, and (3) the parallelogram condensers, which are used only for hand pressure compaction and have nib faces that measure approximately 0.5 to 1 mm.

Condenser shanks may be straight, monangled, or offset, and their nib faces may be cut perpendicular to the long axis of the handle or perpendicular to the end portion of the shank (Online Fig. 22-6). The smaller the nib face size (i.e., area), the greater the pounds per square inch delivered (given a constant malleting force). If the nib diameter is reduced by half, the effective compaction force in pounds per square inch is four times greater (because the area of a circle is proportional to the square of the diameter). For most gold, the 0.4- to 0.55-mm diameter nibs are suitable. Smaller condensers tend to punch holes in the gold, whereas larger ones are less effective in forcing the gold into angles in the tooth preparation.

Two fundamental principles involved in compaction of cohesive gold are to (1) weld the gold into a cohesive mass and (2) wedge as much gold as possible into the tooth preparation.15 Welding takes place primarily as a result of the coherence of the noble metal to itself. Wedging results from careful compacting technique. Regardless of the technique used, some bridging occurs, resulting in void spaces not only in the compacted gold but also along the preparation walls. Success depends on minimizing these voids, particularly on the surface of the restoration and at the cavosurface interface, where leakage to the internal aspects of the restoration may begin. Gold foil compacts readily because of its thin form and produces a mass with isolated linear channels of microporosity (Online Fig. 22-7). Because the thin folds of the gold pellet weld to each other, the remaining channels of microporosity do not appear to be entirely confluent with one another.

It is recommended that compaction of E-Z Gold be done by hand pressure. As compaction is performed, the bag of atomized gold is opened, and the spheres of gold powder move over one another and against the preparation walls. Heavy and methodic hand pressure with the condensers is required to compact this form of gold effectively.

Compaction Technique for Gold Foil

Compaction begins when a piece of gold is placed in a tooth preparation. The gold is first pressed into place by hand, then a condenser of suitable size is used to begin malleting in the center of the mass (often this is done while this first increment is held in position with a holding instrument). Each succeeding step of the condenser overlaps (by half) the previous one as the condenser is moved toward the periphery (Online Fig. 22-8). The gold moves under the nib face of the condenser, effecting compaction as malleting proceeds.

The most efficient compaction occurs directly under the nib face.15 Some compaction also occurs by lateral movement of the gold against surrounding preparation walls. The result of compaction is to remove most of the void space from within each increment of gold, to compact the gold into line and point angles and against walls, and to attach it to any previously placed gold via the process of cohesion.16

The line of force is important when any gold is compacted. The line of force is the direction through which the force is delivered (i.e., the direction in which the condenser is aimed) (Online Fig. 22-9). Specific instructions regarding line of force are given in subsequent sections as they relate to the restorations.

Research has shown that a biologically acceptable pulpal response occurs after proper direct gold procedures.17 Care is required when condensing forces are applied to preclude pulpal irritation. The Electro-Mallet is an acceptable condenser if the manufacturer’s instructions for mallet intensity are followed. Correct hand-malleting technique requires a light, bouncing application of the mallet to the condenser, rather than delivery of heavy blows.

Principles of Tooth Preparation for Direct Gold Restorations

Fundamentals of Tooth Preparation

The principles of tooth preparation for all direct gold restorations demand meticulous attention to detail for success. Failure to give attention to outline form may result in an unsightly restoration or, at the least, one in which cavosurface deficiencies are immediately obvious. Poor resistance form can result in tooth fracture; inadequate retention form may result in a loose restoration that is frustrating to the dentist. Lack of detailed convenience form may render an otherwise excellent tooth preparation unrestorable. The preparation must be smoothed and debrided to permit the first increments of gold to be stabilized.

The margins in outline form must not be ragged. They are established on sound areas of the tooth that can be finished and polished. The outline must include all structural defects associated with the lesion. The marginal outline must be designed to be esthetically pleasing because the final restoration may be visible.

Resistance form is established by orienting preparation walls to support the integrity of the tooth, such as a pulpal wall that is flat and perpendicular to occlusal forces. All enamel must be supported by sound dentin. Optimally placed axial or pulpal walls promote the integrity of the restored tooth, providing a suitable thickness of remaining dentin.

The retention form is established by parallelism of some walls and by strategically placed converging walls (as described in detail for each tooth preparation). In addition, walls must be smooth and flat, where possible (to provide resistance to loosening of the gold during compaction), and internal line angles must be sharp (to resist movement). Internal form includes an initial depth into dentin, ranging from 0.5 mm from the dentinoenamel junction (DEJ) in class I preparations to 0.75 mm from cementum in Class V preparations.

Optimal convenience form requires suitable access and a dry field provided by the rubber dam. Access additionally may require the use of a gingival retractor for Class V restorations or a separator to provide a minimal amount of separation (0.5 mm maximum) between anterior teeth for Class III restorations. Sharp internal line and point angles are created in dentin to allow convenient “starting” gold foil as compaction begins. Rounded form is permitted when E-Z Gold is used to begin the restorative phase. Removal of remaining carious dentin, final planing of cavosurface margins, and debridement complete the tooth preparation for direct gold.

Indications and Contraindications

Class I direct gold restorations are one option for the treatment of small carious lesions in pits and fissures of most posterior teeth and the lingual surfaces of anterior teeth. Direct gold also is indicated for treatment of small, cavitated Class V carious lesions or for the restoration, when indicated, of abraded, eroded, or abfraction areas on the facial surfaces of teeth (although access to the molars is a limiting factor). Class III direct gold restorations can be used on the proximal surfaces of anterior teeth where the lesions are small enough to be treated with esthetically pleasing results. Class II direct gold restorations are an option for restoration of small cavitated proximal surface carious lesions in posterior teeth in which marginal ridges are not subjected to heavy occlusal forces (e.g., the mesial or distal surfaces of mandibular first premolars and the mesial surface of some maxillary premolars). Class VI direct gold restorations may be used on the incisal edges or cusp tips. A defective margin of an otherwise acceptable cast gold restoration also may be repaired with direct gold.

Direct gold restorations are contraindicated in some patients whose teeth have very large pulp chambers, in patients with severely periodontally weakened teeth with questionable prognosis, in patients for whom economics is a severely limiting factor, and in handicapped patients who are unable to sit for the long dental appointments required for this procedure. Root canal–filled teeth are generally not restored with direct gold because these teeth are brittle, although in some cases gold may be the material of choice to close access preparations (for root canal therapy) in cast gold restorations.

Tooth Preparations and Restorations

This section presents the preparation and the restoration of Class I, V, and III lesions. The preparations described may be restored entirely with pellets of gold foil, or E-Z Gold may be used. If powdered gold is selected, heavy hand pressure compaction may be substituted for hand mallet or automatic mallet techniques. Class I and V E-Z Gold restorations may be veneered with gold foil pellets, if desired. The Class III tooth preparation discussed in this chapter is recommended by Ferrier, and only pellets of gold foil are used for the restoration. All tooth preparations and restorative procedures are accomplished after a suitable field of operation has been achieved (usually by application of rubber dam).

Class I Tooth Preparation and Restoration

Tooth Preparation Design

The marginal outline form for the Class I tooth preparation for compacted gold is extended to include the lesion on the tooth surface treated and any fissured enamel. The preparation outline may be a simple circular design for a pit defect, or it may be oblong, triangular, or a more extensive form (if needed to treat a defective fissure) (Online Fig. 22-10, A). Preparation margins are placed beyond the extent of pits and fissures. All noncoalesced enamel and structural defects are removed; the outline is kept as small as possible, consistent with provision of suitable access for instrumentation and for manipulation of gold.

For Class I tooth preparations, the external walls of the preparation are parallel to each other. In extensive occlusal preparations, the mesial or distal wall (or both) may diverge slightly occlusally, however, to avoid undermining and weakening marginal ridges. The pulpal wall is of uniform depth, parallel with the plane of the surface treated, and established at 0.5 mm into dentin. The pulpal wall meets the external walls at a slightly rounded angle created by the shape of the bur. Small undercuts may be placed in dentin if additional retentive features are required to provide convenience form in beginning the compaction of gold (see Online Fig. 22-10, B). Undercuts, when desired, are placed facially and lingually in posterior teeth (or incisally and gingivally on the lingual surface of incisors) at the level of the ideal pulpal floor position. These undercut line angles must not undermine marginal ridges. A slight cavosurface bevel may be placed to (1) create a 30- to 40-degree metal margin for ease in finishing the gold and (2) remove remaining rough enamel. The bevel is not greater than 0.2 mm in width and is placed with a white rotary stone or suitable finishing bur.

Instrumentation

For description and illustration, the preparation of a carious pit on the mandibular first premolar is presented (Online Fig. 22-11, A). By use of a high-speed handpiece with air-water spray, the No. 330 or No. 329 bur is aligned, and the outline form (which includes the limited initial depth) is established (see Online Fig. 22-11, B). When the preparation is extensive because of the inclusion of fissured enamel, a small hoe (imageimage–9) may be used to complete the desired degree of flatness of the pulpal wall. With a No. image bur at low speed, small retentive undercuts are prepared into the dentinal portion of the external walls at the initial pulpal wall depth; these also may be prepared using a image-(90)-image-9 angle-former chisel. Round burs of suitable size are used to remove any infected carious dentin that remains on the pulpal wall. The preparation is completed by finishing the cavosurface with an angle former, a small finishing bur (e.g., No. 7802), or a flame-shaped white stone (see Online Fig. 22-11, C through E).

Restoration

The restorative phase begins with the insertion of a pellet of E-Z Gold or gold foil. The gold is first degassed in the alcohol flame, cooled in air for a few moments, and inserted into the preparation with the passing instrument. The gold is pressed into place with the nib of a small round condenser. In larger preparations, a pair of condensers is used for this initial stabilization of the gold. Next, compaction of the gold begins with a line of force directed against the pulpal wall (Online Fig. 22-12, A). Hand pressure is used for E-Z Gold; malleting is used for gold foil. The gold is compacted into the pulpal line angles and against the external walls, and the line of force is changed to a 45-degree angle to the pulpal and respective external walls (to compact the gold best against the internal walls) (see Online Fig. 22-12, B). Additional increments of gold are added, and the procedure is repeated until the preparation is about three quarters full of compacted gold. If E-Z Gold is to be the final restoration surface, compaction is continued until the restoration is slightly overfilled.

Stay updated, free dental videos. Join our Telegram channel

Jan 9, 2015 | Posted by in Operative Dentistry | Comments Off on 22: Direct Gold Restorations

VIDEdental - Online dental courses

Get VIDEdental app for watching clinical videos